Abstract

Sodium-montmorillonite (Na+-MMT) was intercalation modified with octadecyl trimethyl ammonium bromide (OTAB) in aqueous suspension via an ion exchange mechanism. Fourier transform infrared spectroscopy (FTIR) study indicates that OTAB is successfully intercalated into Na+-MMT layers and/or adsorbed on the surface of Na+-MMT. X-ray diffraction (XRD) analysis revealed that the interlayer spacing of the Na+-MMT was extended with the content of OTAB increasing, and the maximum spacing can reach about 3.80 nm. Results of scanning electron microscopy (SEM) analysis reveals the morphologies change from spherical-like particles to high-aspect ratio flakes after modification. Different configurations of OTA+ chains within MMT interlayer are proposed based on the above analysis. The results of contact angle and the dispersion analysis show that the surface wettability of Na+-MMT is converted from hydrophilic to organophilic.

Bahasa Abstract

Sodium-montmorilonit (Na + -MMT) adalah interkalasi yang dimodifikasi dengan oktadekil trimetil amonium bromida (OTAB) dalam suspensi air melalui mekanisme pertukaran ion. Penelitian spektroskopi inframerah Fourier (FTIR) menunjukkan bahwa OTAB berhasil diselingi lapisan Na + -MMT dan / atau teradsorpsi pada permukaan Na + -MMT. Analisis difraksi sinar-X (XRD) menunjukkan bahwa jarak interlayer Na + -MMT diperpanjang dengan kandungan OTAB meningkat, dan jarak maksimum bisa mencapai sekitar 3,80 nm. Hasil analisis mikroskop elektron scanning (SEM) menunjukkan perubahan morfologi dari partikel mirip bola hingga flut rasio aspek tinggi setelah modifikasi. Berbagai konfigurasi rantai OTA + dalam interlayer MMT diusulkan berdasarkan analisis di atas. Hasil sudut kontak dan analisis dispersi menunjukkan bahwa kesetimbangan permukaan Na + -MMT diubah dari hidrofilik menjadi organofilik.

Download

Share

COinS