Galvanized steel sheet of 0.8 mm in thickness was drilled with circle holes of 2.5 mm diameter and spacing arranged in tetragonal and hexagonal pattern. The manufacturing properties of specimen were studied through drawing and stretching simulative test. It was concluded from the results that, at high ratio of punch to hole diameter (40/2.5), the drawing properties (LDR) of both square and hexagonal perforated sheet were slightly lower than that of solid sheet, while hexagonal perforated showing LDR somewhat higher than the square one. The stretching properties (LDH) of sheet, however, were much lower than that of solid sheet while the hexagonal perforated exhibiting LDH lower than the square one. Provided the effi ciency factor was well defi ned, which was not effective in the present experiment, the intrinsic drawing properties might be indirectly determined through the simulative test by assuming the perforated materials as an equivalent continuum.

Bahasa Abstract

Spesimen uji lembaran baja galvanis dengan tebal 0.8 mm diberi lubang lingkaran berdiamater dan antar lubang 2.5 mm dengan pola susunan tetragonal dan heksagonal. Sifat manufaktur bahan tersebut dipelajari melalui pengujian simulatif penarikan (drawing) dan rentang (stretching). Sebagai pembanding, dilakukan pengujian terhadap lembaran sejenis tanpa lubang perforasi. Dari hasil penelitian ini diketahui perbandingan sifat manufaktur lembaran perforasi dengan pola susunan lubang tetragonal dan heksagonal serta prediksi sifat intrinsik mampu tarik lembaran perforasi dengan menggunakan asumsi kontinum ekivalen.


R. Kopp. J. of Mat. Proc. Technology 60 (1996) 1.

R. Kopp, A. Schmitz. J. of Mat. Proc. Technology 59 (1996) 186.

Y. Nakamura, T. Tatenami, T. Ohata, In: Proc. of the 3th Int. Conference on Technology of Plasticity 3, Advanced Technology of Plasticity 1 [6] 1990, p.1231.

F.K. Chen. J. of Mat. Proc. Technology 37 (1993) 175.

Operating Instruction of 12tf Automatic Universal Deeo Draw Tester (SAS-12). Tokyo Testing Machine Manufactory Co., Ltd.

W. Muzykiewics, K. Swiatkwoski, P. Domagala, In: Proc. of the First Australisian Congress on Applied Mechanics 2 [21-23] (1996) p.907.

Kurt Lange, Hand Book of Metal Forming. McGraw- Hill Book Co. New York, 1985.

George. E. Dieter, Mechanical Metallurgy 2nd ed., Mc.Graw Hill Book, Co., Singapore, 1984.

W. F. Hosford, Robert M. Caddel, Metal Forming: Mechanics and Metallurgy, Prentice Hall, New Jersey,1983.

J.N. Harris, Mechanical Working of Metals: Theory



To view the content in your browser, please download Adobe Reader or, alternately,
you may Download the file to your hard drive.

NOTE: The latest versions of Adobe Reader do not support viewing PDF files within Firefox on Mac OS and if you are using a modern (Intel) Mac, there is no official plugin for viewing PDF files within the browser window.